We present a brief résumé of the history of solidification research and key factors affecting the solidification of fusion welds. There is a general agreement of the basic solidification theory, albeit differing - even confusing - nomenclatures do exist, and Cases 2 and 3 (the Chalmers' basic boundary conditions for solidification, categorized by Savage as Cases) are variably emphasized. Model Frame, a tool helping to model the continuum of fusion weld solidification from start to end, is proposed. It incorporates the general solidification models, of which the pertinent ones are selected for the actual modeling. The basic models are the main solidification Cases 1…4. These discrete Cases are joined with Sub-Cases: models of Pfann, Flemings and others, bringing needed Sub-Case variables into the model. Model Frame depicts a grain growing from the weld interface to its centerline. Besides modeling, the Model Frame supports education and academic debate. The new mathematical modeling techniques will extend its use into multi-dimensional modeling, introducing new variables and increasing the modeling accuracy. We propose a model: melting/solidification-model (M/S-model) - predicting the solute profile at the start of the solidification of a fusion weld. This Case 3-based Sub-Case takes into account the melting stage, the solute back-diffusion in the solid, and the growth rate acceleration typical to fusion welds. We propose - based on works of Rutter & Chalmers, David & Vitek and our experimental results on copper - that NEGS-EGS-transition is not associated only with cellular-dendritic-transition. Solidification is studied experimentally on pure and doped copper with welding speed range from 0 to 200 cm/min, with one test at 3000 cm/min. Found were only planar and cellular structures, no dendrites - columnar or equiaxed. Cell sub structures: rows of cubic elements we call "cubelettes", "cell-bands" and "micro-cells", as well as an anomalous crack morphology "crack-eye", were detected, as well as microscopic hot crack nucleus we call "grain-lag cracks", caused by a grain slightly lagging behind its neighbors in arrival to the weld centerline. Varestraint test and R-test revealed a change of crack morphologies from centerline cracks to grainand cell boundary cracks with an increasing welding speed. High speed made the cracks invisible to bare eye and hardly detectable with light microscope, while electron microscope often revealed networks of fine micro-cracks.